压力单位换算和腐蚀材质表
更新时间：2008-09-23 点击次数：2712
|
压力单位换算表
|
|
单位
|
Pa
|
KPa
|
MPa
|
bar
|
mbar
|
kgf/cm2
|
cmH2O
|
mmH2O
|
mmHg
|
p.s.i
|
|
Pa
|
1
|
10-3
|
10-6
|
10-5
|
10-2
|
10.2×
10-6
|
1.02×10-3
|
101.97×
10-3
|
7.5×
10-3
|
0.15×10-3
|
|
KPa
|
103
|
1
|
10-3
|
10-2
|
10
|
10.2×
10-3
|
10.2
|
101.97
|
7.5
|
0.15
|
|
MPa
|
06
|
103
|
1
|
10
|
104
|
10.2
|
1.02×103
|
101.97×103
|
7.5×103
|
0.15×103
|
|
bar
|
105
|
102
|
10-1
|
1
|
103
|
1.02
|
1.02×103
|
10.2×103
|
750.06
|
14.5
|
|
mbar
|
102
|
10-1
|
10-4
|
10
|
1
|
1.02×
10-3
|
1.02
|
10.2
|
0.75
|
14.5×10-3
|
|
kgf/cm2
|
98066.5
|
98.07
|
98.07×
10-3
|
0.98
|
980.67
|
1
|
1000
|
10.000
|
735.56
|
14.22
|
|
cmH2O
|
98.06
|
98.07×
10-3
|
98.07×
10-6
|
0.98×
10-3
|
0.98
|
10-3
|
1
|
10
|
0.74
|
14.22×103
|
|
mmH2O
|
9.806
|
9.807×
10-3
|
9.807×
10-6
|
98.07×
10-6
|
98.07×
10-3
|
10-4
|
0.1
|
1
|
73.56×
10-3
|
1.42×10-3
|
|
mmHg
|
133.32
|
133.32×
10-3
|
133.32×
10-6
|
1.33×
10-3
|
1.33
|
1.36×
10-3
|
1.36
|
13.6
|
1
|
19.34×10-3
|
|
p.s.i
|
6894.76
|
6.89
|
6.89×
10-3
|
68.95×
10-3
|
68.95
|
70.31×
10-3
|
70.31
|
703.07
|
51.71
|
1
|
|
|
|
|
|
关于隔离膜片部分耐蚀材料的选择
|
|
腐蚀介质
|
耐腐蚀材料
|
|
锡青铜(QSn6.5-0.4)
|
SUS316
|
纯钽(Ta)
|
蒙耐尔(Ni70Cu30)
|
哈氏合(HC)
|
聚四氟乙烯（F4）
|
|
硫酸（H2SO4）
|
V
|
△
|
○
|
V
|
V
|
V
|
|
硝酸（HNO3）
|
╳
|
V
|
○
|
╳
|
V
|
V
|
|
盐酸（HCI）
|
△
|
╳
|
○
|
╳
|
V
|
V
|
|
磷酸（H3PO4）
|
V
|
V
|
○
|
V
|
V
|
V
|
|
醋酸（CH3COOH）
|
V
|
V
|
○
|
V
|
○
|
V
|
|
烧碱（NaOH）
|
△
|
○
|
△
|
○
|
○
|
V
|
|
纯碱（Na2CO3）
|
○
|
○
|
○
|
○
|
V
|
V
|
|
小苏打（NaHCO3）
|
V
|
○
|
○
|
○
|
○
|
V
|
|
氯气（CI）
|
干：V
湿：╳
|
干：V
湿：╳
|
○
|
干：V
湿：╳
|
V
|
V
|
|
溴（Br2）
|
干：△
湿：╳
|
干：╳
湿：△
|
○
|
干：○
湿：╳
|
○
|
V
|
|
氨水（NH3）
|
╳
|
V
|
╳
|
╳
|
○
|
V
|
|
海水（30％ NaCI）
|
V
|
V
|
○
|
○
|
○
|
V
|
|
符号说明：○——*；△——有条件使用；V——可以使用；╳——不可以使用。
|
本公司一般的选用材料为SUS316-0Cr17Ni12m，以上耐蚀材料选择为常温情况，对在特殊情况下耐蚀材料的选择请与我公司具体垂询。
|
|